Pelton Turbine Generator China

Forging could considerably improve metal's organizational structure and
mechanical property.  
Forging offers uniformity of composition and structure. Forging results in
metallurgical recrystalisation and grain refinement as a result of the thermal
cycle and deformation process. This strengthens the resulting steel product
particularly in terms of impact and shear strength.Forged steel is generally
stronger and more reliable than castings part.

Project Basic Information
Project Name: Minas-San Francisco HPP
Project Location: Ecuador
Pelton runner pitch diameter: 2460mm.
OD: 3179mm
Net Weight: 13300KG
Buckent No. 21
Output: 91.6MW
Product Introduction
1. Brief introduction for Forged Integrally +100% CNC Machined Pelton Turbine
Runner
Forging could considerably improve metal’s organizational structure and
mechanical property.  
Forging offers uniformity of composition and structure. Forging results in
metallurgical recrystalisation and grain refinement as a result of the thermal
cycle and deformation process. This strengthens the resulting steel product
particularly in terms of impact and shear strength.
Forged steel is generally stronger and more reliable than castings of same
material due to the fact that the grain flows of the steel are altered,
conforming to the shape of the part.
Getai Hydropower is Pelton Turbine Experiment, Francis Turbine Diagram, Francis
Turbine Working, Pelton Turbine For Sale factoty.
Performance comparison table of forging parts and casting parts
 Performance test of forging part
Mechanical Property σb(Mpa) σ0.2(Mpa) δ5(%) ψ(%)
AKV(J/cm²) HB
Standard value ≥795 ≥620 ≥15 ≥45 ≥50 230~295
Actual value Horizontal 815 655 17.5 64.5 107 102
110 259 256 253
Vertical 820 660 18.5 67 149 152 136
256 257 257
 
Performance test of casting part
Mechanical Property σb(Mpa) σ0.2(Mpa) δ5(%) ψ(%)
AKV(J/cm²) HB
Standard value ≥750 ≥550 ≥15 ≥35 ≥50 221~286
Actual value 770 610 17 50 84 88 85 252
255 254

2. Machining vedio for the Forged entire CNC machined Pelton runner.  
3. ISO 9001 Quality Management system is carried out to ensure better
management control
4. Advanced CFD, FEA technic is utilized in the designing process to ensure
better technical solution.
5. CAE casting simulation is adopted for the produciton of casting parts,
this advanced and reliable process plan could help effectively improve product
quality.
6. All raw material strictly conform to international standard, key component
such as runners, guide vane is Forged and entire CNC machined

Minimum Order: 1 tons

Pelton Turbine Generator China
Enlarge Click to Enlarge
SOURCE: Import-Export Bulletin Board (http://www.imexbb.com/)