PA66 GF15 (A2000C)

PA66 GF 15 is Nylon66 and 15% Glass-Filled, these materials are performed with
medium stiffness and strength but it has much better mechanical properties over
unfilled granules. Reinforced with 15% of glass fiber and modified Nylon 66 in
Anmei plastic plant combined with other property enhancements such as high
tensile strength, heat stabilized and flame retardant make it suitable for
injection molding. 
Other percentages glass-filled nylon is also available on a custom-order basis.
Typical Application of pa66gf15 (A2000C)
Nylon 66 GF15, mainly used in internal and external structural parts around the
engine, electrical switches, and electronic connectors.
Processing Detail of PA66 GF15 (A2000C)

Other Details of pa6 6gf15 (A2000C)
Physical Property
Ash (15.0% 1 ISO3451/1)
Conditioned 600°C*2h
Density (1245Kg/m3 1 ISO1183)
Conditioned 23°C
Shrinkage Parallel Flow (0.7-1.0% 1 ISO294-4)
Shrinkage Vertical Flow (1.0-1.4% I ISO294-4)
Mechanical Properties
Tensile strength (125.0MPa 1 ISO527)
Conditioned 5mm/ min
Tensile Strain at Break (2.0% I ISO527)
Conditioned 5mm/min
Notched Impact Strength 6.0KJ/m2 ISO179)
Conditioned 1.0J
Flexural Strength (188MPa 1ISO178)
Conditioned 2mm/min
Flexural Modulus (5350MPa I ISO178)
Conditioned 2mm/ min
Thermal Property
Melting Point (260°C I ISO11357)
Hot Deformation Temperature (240*C I ISO75)
Conditioned 1.8MPa
Flammability Class (HB 1UL94)
Conditioned mm
Injection Molding Conditions
Drying Temperature 130°C
Drying Time 3h
Cylinder Temperature 280-300°C
Nozzle Temperature 280-300*C
Tooling Temperature 80-100*C
* Molding conditions are just for reference, please make an adjustment based
on the actual situation！
Want to know the details of modified polyolefin or more, contact us.