PTFE Fine Powder/RR:100:1/Tape Application/Paste Extrusion

Product Description
PTFE Fine Powder/RR:100:1/Tape Application/Paste Extrusion 0

Everflon Fluoropolymer PTFE Fine Powder


Everflon® PTFE Fine Powder F100 is a polytetrafluoroethylene fine powder resin used
primarily for paste extrusion. Everflon® PTFE F100 offers the excellent combination
of properties typical of Everflonfluoroplastic resins:

• Non-aging characteristics

• Chemical inertness tonearly all industrial chemicals and solvents

• Exceptional dielectric properties, stable with frequency and temperature

•Toughness and flexibility

• Low coefficient of friction

• Non-stick characteristics

• Negligible moisture absorption

• Excellent weather resistance

• Service temperature up to 260 °C (500 °F)

• Useful properties at –240 °C (–400 °F)

• Moderate stiffness and high ultimate elongation

Compared with other grades of PTFE fine powder,Everflon PTFE F500 is a premium
resin that has increased thermal stability, superior flex life, superior stress
crack resistance, low permeability, and high clarity.

Everflon PTFE F100is designed for processing at low to medium reduction ratios of
10:1 to 300:1. It is designed to facilitate the production of high-quality, low-
density tape and beading.

Everflon PTFE F100 meets the requirements of ASTM D4895,



Main Porperties Everflon Fluoropolymer PTFE Fine Powder F100


PTFE Fine Powder/RR:100:1/Tape Application/Paste Extrusion 1









Main Application of Everflon Fluoropolymer PTFE F100




Everflon™ PTFE F100 is widely used for conformable, high performance sealing
materials and as tape for wire and cable insulation.








Processing




, Everflon™ PTFE F100 is extruded using a liquid processing aid such as naphtha. In
the paste extrusion process, the powder is mixed with a lubricant aid and then
compressed into a cylindrical preform slug under light pressure (1.5–2.0 MPa
[220–290 psi]).






The preform slug is placed in the cylinder of a paste extruder, where the
composition is forced under high pressure through a finishing die to produce
beading, tubing, or wire coatings.



After extrusion, the product is a low-density, but coherent, fibrous structure.
After removal of the lubricant by heating within the range of 100–300 °C (212–
572 °F), the extrudate can be either


sintered above its melting point of around 345 °C (653 °F) to produce a void-free
PTFE article or calendered and stretched to produce unsintered or semisintered
articles.
PTFE Fine Powder/RR:100:1/Tape Application/Paste Extrusion
Enlarge Click to Enlarge
SOURCE: Import-Export Bulletin Board (https://www.imexbb.com/)
Report Abuse

Post an Offer to Sell

© 1996-2010 IMEXBB.com. All rights reserved.

IMEXBB.com