Silver Mechanical Zinc Flake Coating Geomet Anti Corrosion For Brake Disc

Chrome free water based zinc flake coating for brake disc PH 5.0-7.5 Viscosity
25~40s ( Spray Coating )

Product Description:

JH-9310G is made up of three packs: A,B and C;
Pack A: It is silver gray slurry that mainly chemically combined with super fine
flake Zn, super fine flake Al and organic additive.
Pack B: It is water solution that mainly combined with corrosion protecion
additive, particular regulator water solution etc.
Pack C: It is the tackifier of the coating which mainly made up of cellulose white
or yellowish powder.


Performance Charcteristic:

Chrome free , film is silver grey to silver white, better corrosion protection
performance.Environmentally friendly products, film is silver, has good corrosion
resistance, the use of technology is almost equivalent to the JUNHE of dacroment.


Coating Process

1. Mix Ratio
Pack A: Pack B: Pack C=1:1: X(according to different viscosity demand )

2. Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A
to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly
dispersed, reduce the agitating speed to 60r/min, and add B.

3. Add B to the stirring A slowly.

4. Stir the mixture about 1~2 hours after B added, then add C. C should be powdered
if lump exist.(The barrel temperature should not be lower than 20℃, otherwise C
will not be dissolved sufficiently .)Then stir 10~12 hours alowly and continuously.


Technical data:


No. Item Data
1 Color Silver
2 Coating method spraying
3 PH 5.0-7.5
4 Specific gravity 1.40±0.1
5 Viscosity 25~40s(Spray Coating)


Mix Diagram:

Silver Mechanical Zinc Flake Coating Geomet Anti Corrosion For Brake Disc 0

Caution: Temperature should be controlled in above operation.


Coating Process:

Silver Mechanical Zinc Flake Coating Geomet Anti Corrosion For Brake Disc 1


Attentions:

1. Other chemicals such as any kinds of acid, alkali salt can not be mixed into
coating, for these can activate Zn & Al plate to aging the coating.
2. Avoid irradiation of sunshine and ultraviolet ray for long time when operating,
otherwise it will accelerate aging or polymerization of the coating .
3. It is very important to control the temperature of coating. If the temperature
of coating changes when operating, it will effect the viscosity, then effec the
coating quatity on workpiece. So the relations among temperature,viscosity and
spinning process shoud be controlled well when coating.
4. The viscosity will be different if coating method is different. Choose low data
if spray coating,and choose high data if dip spin coating.

Click to Enlarge